{"id":6032,"date":"2026-09-02T23:10:00","date_gmt":"2026-09-02T23:10:00","guid":{"rendered":"https:\/\/beiyutitanium.com\/?p=6032"},"modified":"2026-09-02T23:55:10","modified_gmt":"2026-09-02T23:55:10","slug":"titanium-in-nitric-acid","status":"publish","type":"post","link":"https:\/\/beiyutitanium.com\/es\/titanium-in-nitric-acid\/","title":{"rendered":"Titanio en \u00e1cido n\u00edtrico: tasas, m\u00e1ximo en el intervalo intermedio y l\u00edmites estrictos"},"content":{"rendered":"

En \u00e1cido n\u00edtrico al 90 por ciento en ebullici\u00f3n sobre una superficie de calentamiento, los ensayos publicados por TIMET sit\u00faan el titanio sin alear entre 1.0 y 6.6 mpy (0.03 a 0.17 mm\/y), mientras que el acero inoxidable Type 304L registr\u00f3 entre 150 y 2900 mpy (3.8 a 73.7 mm\/y) en los mismos ensayos de TIMET. Esa diferencia de dos a tres \u00f3rdenes de magnitud explica por qu\u00e9 el servicio con \u00e1cido n\u00edtrico es uno de los casos m\u00e1s favorables para el titanio. Pero los mismos datos muestran dos aspectos que el dise\u00f1ador debe conocer: la velocidad de corrosi\u00f3n alcanza su m\u00e1ximo en la zona media del intervalo de concentraci\u00f3n, no en su extremo superior, y el \u00e1cido n\u00edtrico fumante rojo constituye una exclusi\u00f3n estricta.<\/p>\n

Titanio frente a acero inoxidable sobre una superficie calefactora<\/h2>\n
\n\n\n\n\n\n\n\n
Corrosi\u00f3n de superficies calefactoras de titanio y acero inoxidable expuestas a \u00e1cido n\u00edtrico al 90 por ciento en ebullici\u00f3n a 215 F, seg\u00fan el manual publicado de resistencia a la corrosi\u00f3n del titanio de TIMET. Las temperaturas del metal corresponden a la superficie calentada, no al \u00e1cido en el volumen principal.<\/caption>\n
Temperatura del metal<\/th>\nTitanio sin alear<\/th>\nAcero inoxidable Type 304L<\/th>\n<\/tr>\n<\/thead>\n
240 F (116 C)<\/td>\n1.1 a 6.6 mpy (0.03 a 0.17 mm\/y)<\/td>\n150 a 518 mpy (3.8 a 13.2 mm\/y)<\/td>\n<\/tr>\n
275 F (135 C)<\/td>\n1.6 a 6.1 mpy (0.04 a 0.15 mm\/y)<\/td>\n676 a 2900 mpy (17.2 a 73.7 mm\/y)<\/td>\n<\/tr>\n
310 F (154 C)<\/td>\n1.0 a 2.3 mpy (0.03 a 0.06 mm\/y)<\/td>\n722 a 2900 mpy (18.3 a 73.7 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Interprete la columna de acero inoxidable como el motivo por el que se especifica titanio para el equipo. Dos l\u00edmites francos de esa comparaci\u00f3n. Type 304L no es lo que una planta de \u00e1cido n\u00edtrico especificar\u00eda realmente a esta temperatura: los competidores reales son los austen\u00edticos con silicio, como UNS S30600, y, por encima de aproximadamente el 80 por ciento de \u00e1cido, el aluminio. E interprete la columna de titanio como lo que es: una condici\u00f3n de superficie calefactora, en ebullici\u00f3n, a una concentraci\u00f3n, m\u00e1s severa que el servicio en el volumen principal de l\u00edquido a la misma temperatura.<\/p>\n

La parte contraintuitiva: la peor concentraci\u00f3n est\u00e1 en el medio<\/h2>\n

Los ingenieros que empiezan a trabajar con titanio suelen suponer que un \u00e1cido m\u00e1s concentrado implica un ataque m\u00e1s r\u00e1pido. En \u00e1cido n\u00edtrico puro en ebullici\u00f3n, en fase l\u00edquida, la curva publicada hace lo contrario. La tasa de corrosi\u00f3n aumenta desde cerca de cero al 10 por ciento y vuelve a disminuir hacia el 70 por ciento, con el m\u00e1ximo entre ambos. En la curva de TIMET, las calidades sin alear y con paladio alcanzan m\u00e1ximos de alrededor de 24 a 26 mpy (0.61 a 0.66 mm\/y) en alg\u00fan punto entre el 40 y el 50 por ciento en peso, mientras que Grade 12 alcanza su m\u00e1ximo antes y a menor nivel, cerca de 15 mpy (0.38 mm\/y), y se mantiene por debajo en toda la parte intermedia del intervalo.<\/p>\n

La consecuencia pr\u00e1ctica: en esa curva de ebullici\u00f3n de \u00e1cido puro, una columna o un rehervidor que funciona toda su vida con \u00e1cido al 35 por ciento est\u00e1 sometido a un servicio m\u00e1s exigente que uno al 65 por ciento, y un proceso que oscila por la banda intermedia es m\u00e1s exigente que cualquiera de ellos. Indique el intervalo de concentraci\u00f3n, no solo el m\u00e1ximo.<\/p>\n

La cifra para dimensionar el espesor de pared<\/h2>\n

Antes de continuar, conviene indicar claramente en qu\u00e9 coinciden y en qu\u00e9 difieren los datos publicados, porque esta p\u00e1gina presenta dos cifras para lo que parece ser el mismo servicio. Para titanio sin alear en \u00e1cido en ebullici\u00f3n cerca del 68 al 70 por ciento:<\/p>\n

\n\n\n\n\n\n\n
Fuente dentro del mismo manual<\/th>\nTasa<\/th>\n<\/tr>\n<\/thead>\n
La curva de concentraci\u00f3n en ebullici\u00f3n para \u00e1cido puro, le\u00edda al 70 por ciento. L\u00edquido en ebullici\u00f3n, probeta sin calentar; duraci\u00f3n de exposici\u00f3n no indicada en la fuente citada<\/td>\nAproximadamente 5 mpy (0,13 mm\/y)<\/td>\n<\/tr>\n
La tabla de titanio disuelto, l\u00edquido al 68 por ciento en ebullici\u00f3n sin presencia de ion de titanio, ensayo de 24 horas<\/td>\n31.8 mpy (0.81 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Son referencias de ensayo diferentes, y la dispersi\u00f3n no es un error en ninguna de ellas. Es la dispersi\u00f3n real en este servicio, y otros datos del propio manual sit\u00faan el \u00e1cido al 70 por ciento en ebullici\u00f3n en un intervalo aproximado de 2.5 a 37 mpy (0.064 a 0.94 mm\/y), tambi\u00e9n sin duraci\u00f3n de exposici\u00f3n indicada. La regla de dise\u00f1o que se deriva es la parte importante de esta p\u00e1gina: dimensione el espesor de pared seg\u00fan la tasa del \u00e1cido puro sin inhibici\u00f3n, del orden de 0,8 mm al a\u00f1o en la peor concentraci\u00f3n, y considere la inhibici\u00f3n por iones met\u00e1licos como margen, no como base de dise\u00f1o.<\/strong> El motivo se encuentra en la siguiente secci\u00f3n: varios puntos de una planta real est\u00e1n expuestos a \u00e1cido que no contiene ning\u00fan ion inhibidor.<\/p>\n

Los cationes met\u00e1licos disueltos inhiben; otros contaminantes hacen lo contrario<\/h2>\n

El efecto es espec\u00edfico de los cationes met\u00e1licos disueltos. El manual menciona los iones de silicio, cromo, hierro, titanio y metales preciosos como platino y rutenio como inhibidores en cantidades m\u00ednimas. No es una regla general sobre la contaminaci\u00f3n: las sales con cloruros requieren sus propios datos, mientras que una carga elevada de sales de nitrato desplaza la tasa en el sentido contrario y produce las peores cifras del manual para \u00e1cido n\u00edtrico solo. Dentro de ese l\u00edmite, en \u00e1cido n\u00edtrico al 68 por ciento en ebullici\u00f3n, una peque\u00f1a contaminaci\u00f3n de cromo empeor\u00f3 notablemente Type 304L, mientras que el titanio mejor\u00f3:<\/p>\n

\n\n\n\n\n\n\n\n\n\n
Efecto del cromo sobre la corrosi\u00f3n del acero inoxidable y el titanio en \u00e1cido n\u00edtrico al 68 por ciento en ebullici\u00f3n, tres periodos de 48 horas con cambio de \u00e1cido en cada periodo, seg\u00fan el manual publicado de TIMET.<\/caption>\n
Cromo en soluci\u00f3n<\/th>\nType 304L recocido<\/th>\nTitanio sin alear<\/th>\n<\/tr>\n<\/thead>\n
0,0 por ciento<\/td>\n12 a 18 mpy (0.30 a 0.46 mm\/y)<\/td>\n3.5 a 3.8 mpy (0.09 a 0.10 mm\/y)<\/td>\n<\/tr>\n
0,0005 por ciento<\/td>\n12 a 20 mpy (0.30 a 0.51 mm\/y)<\/td>\nNo indicado<\/td>\n<\/tr>\n
0,005 por ciento<\/td>\n60 a 90 mpy (1.5 a 2.3 mm\/y)<\/td>\n0.9 a 1.6 mpy (0.022 a 0.041 mm\/y)<\/td>\n<\/tr>\n
0,05 por ciento<\/td>\n980 a 1600 mpy (24.9 a 40.6 mm\/y)<\/td>\nNo indicado<\/td>\n<\/tr>\n
0,01 por ciento<\/td>\nNo indicado<\/td>\n0.1 a 1.4 mpy (0.003 a 0.036 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

El propio titanio disuelto es un inhibidor a\u00fan m\u00e1s potente de la corrosi\u00f3n del titanio en este servicio:<\/p>\n

\n\n\n\n\n\n\n\n\n\n
Efecto del titanio disuelto sobre la tasa de corrosi\u00f3n del titanio sin alear en \u00e1cido n\u00edtrico en ebullici\u00f3n, ensayos de 24 horas, seg\u00fan el manual publicado de TIMET.<\/caption>\n
Ion de titanio a\u00f1adido<\/th>\nEn HNO3 al 40 por ciento<\/th>\nEn HNO3 al 68 por ciento<\/th>\n<\/tr>\n<\/thead>\n
0 mg\/l<\/td>\n29.5 mpy (0.75 mm\/y)<\/td>\n31.8 mpy (0.81 mm\/y)<\/td>\n<\/tr>\n
10 mg\/l<\/td>\nNo indicado<\/td>\n0.8 mpy (0.02 mm\/y)<\/td>\n<\/tr>\n
20 mg\/l<\/td>\n8.6 mpy (0.22 mm\/y)<\/td>\n2.4 mpy (0.06 mm\/y)<\/td>\n<\/tr>\n
40 mg\/l<\/td>\n1.9 mpy (0.05 mm\/y)<\/td>\n0.4 mpy (0.01 mm\/y)<\/td>\n<\/tr>\n
80 mg\/l<\/td>\n0.8 mpy (0.02 mm\/y)<\/td>\n0.4 mpy (0.01 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

El manual aplica esto a corrientes de recirculaci\u00f3n, como los circuitos de rehervidor de desorbedores, donde la inhibici\u00f3n resulta de alcanzar un nivel estable de titanio disuelto. Hay dos l\u00edmites asociados. Primero, alcanzarlo no es autom\u00e1tico: depende del \u00e1rea mojada, la tasa de corrosi\u00f3n, el volumen del circuito y el caudal de reposici\u00f3n, y el efecto se autolimita, porque a 0.4 mpy el metal libera mucho menos titanio que a 31.8 mpy. Un circuito con mucha reposici\u00f3n se aproxima m\u00e1s a uno de paso \u00fanico de lo que sugiere la palabra recirculaci\u00f3n. Segundo, y m\u00e1s importante para la seguridad, varias partes de una planta real est\u00e1n expuestas a \u00e1cido sin ning\u00fan ion inhibidor: ramales de paso \u00fanico, arranque, el periodo posterior a una sustituci\u00f3n del \u00e1cido o a un lavado, y el condensado, que por este mismo mecanismo es el \u00e1cido m\u00e1s puro del sistema. Comparada con un circuito de recirculaci\u00f3n equilibrado, una probeta de laboratorio en \u00e1cido nuevo sin inhibici\u00f3n puede dar resultados peores, no mejores. Las ubicaciones de paso \u00fanico y transitorias que se acaban de enumerar pueden parecerse a ese caso sin inhibici\u00f3n, por lo que la base de dise\u00f1o anterior utiliza la tasa sin inhibici\u00f3n.<\/p>\n

La fase de vapor es un servicio distinto del l\u00edquido<\/h2>\n
\n\n\n\n\n\n\n\n
Resistencia del titanio a la corrosi\u00f3n por vapores de \u00e1cido n\u00edtrico, muestras suspendidas sobre el aze\u00f3tropo al 70 por ciento en ebullici\u00f3n, exposici\u00f3n de 144 horas, seg\u00fan el manual publicado de TIMET.<\/caption>\n
Calidad<\/th>\nTasa de corrosi\u00f3n<\/th>\n<\/tr>\n<\/thead>\n
Titanio sin alear<\/td>\n2.0 mpy (0.051 mm\/y)<\/td>\n<\/tr>\n
Grade 12 (Ti-0.3Mo-0.8Ni)<\/td>\n0.8 mpy (0.020 mm\/y)<\/td>\n<\/tr>\n
Sin alear con paladio<\/td>\n0.08 mpy (0.002 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

El \u00e1cido en condensaci\u00f3n y el condensado que escurre son los puntos cl\u00e1sicos de fallo en servicio con \u00e1cido n\u00edtrico, y la clasificaci\u00f3n de calidades all\u00ed no es la misma que en el l\u00edquido. Para \u00e1cido caliente muy puro y para servicio de condensaci\u00f3n, la preferencia publicada es Grade 1 sin alear de mayor pureza (UNS R50250), y el motivo es el comportamiento de las uniones soldadas, no la tasa del metal base de esta tabla. Observe tambi\u00e9n qu\u00e9 es y qu\u00e9 no es esta tabla: probetas suspendidas en vapor sobre el aze\u00f3tropo durante 144 horas. No es un ensayo de pel\u00edcula de condensaci\u00f3n, y el manual no asigna ninguna tasa al condensado que escurre en ning\u00fan apartado.<\/p>\n

D\u00f3nde se excluye por completo el titanio<\/h2>\n
\n\n\n\n\n\n\n\n\n\n
Condici\u00f3n<\/th>\nEstado<\/th>\n<\/tr>\n<\/thead>\n
\u00c1cido n\u00edtrico fumante rojo<\/td>\nNo utilizar.<\/strong> El mecanismo publicado no es corrosi\u00f3n simple: el ataque es intergranular y deja un residuo superficial de titanio met\u00e1lico finamente dividido, que es muy pirof\u00f3rico y puede detonar en presencia de un agente oxidante fuerte. El manual indica el intervalo de composici\u00f3n para que se desarrolle la reacci\u00f3n: contenido de agua inferior al 1,34 por ciento y NO2 superior al 6 por ciento, y muestra un \u00e1rea expl\u00edcita de incertidumbre entre las regiones con y sin reacci\u00f3n. Su ap\u00e9ndice identifica por separado el \u00e1cido fumante rojo con menos de aproximadamente el 2 por ciento de agua como sensible a la ignici\u00f3n; por tanto, esta exclusi\u00f3n cubre el \u00e1rea de incertidumbre hasta esa l\u00ednea de aproximadamente el 2 por ciento de agua, no solo las composiciones por debajo del 1,34 por ciento. Compare su an\u00e1lisis con ese intervalo y no con la denominaci\u00f3n, porque una corriente rara vez se denomina fumante roja en la ficha t\u00e9cnica.<\/td>\n<\/tr>\n
\u00c1cido n\u00edtrico fumante blanco<\/td>\nAceptable seg\u00fan el mismo manual, con aproximadamente 0.1 mpy a temperatura ambiente. No interprete que la exclusi\u00f3n del fumante rojo abarca todos los \u00e1cidos fumantes.<\/td>\n<\/tr>\n
\u00c1cido n\u00edtrico con cloruro, hasta agua regia<\/td>\nPeligro cuantificado, que invierte la l\u00f3gica habitual de las calidades. En el ensayo de 96 horas en ebullici\u00f3n con agua regia del manual, tres partes de \u00e1cido clorh\u00eddrico por una de n\u00edtrico, el titanio sin alear y la calidad con paladio registraron ambos 44 mpy (1,12 mm\/y), mientras que Grade 12 registr\u00f3 24 mpy (0,61 mm\/y). Por tanto, la calidad con paladio no present\u00f3 ventaja frente al titanio sin alear, mientras que Grade 12 fue la menor de las tres. A temperatura ambiente, el titanio es esencialmente inmune al agua regia. Las velocidades en mezclas de \u00e1cidos aumentan al aumentar el componente \u00e1cido reductor o la temperatura.<\/td>\n<\/tr>\n
\u00c1cido n\u00edtrico que contiene fluoruros<\/td>\nRequiere revisi\u00f3n. El fluoruro en \u00e1cido puede formar \u00e1cido fluorh\u00eddrico, que ataca r\u00e1pidamente al titanio.<\/td>\n<\/tr>\n
\u00c1cido caliente muy puro y condensado de vapor<\/td>\nPermitido, pero sensible a la calidad. Las tasas aumentan, las uniones soldadas son el elemento expuesto y la preferencia publicada son las calidades sin alear de mayor pureza.<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Una p\u00e1gina de proveedor que solo enumera las filas favorables no sirve para el dise\u00f1o. En particular, la exclusi\u00f3n del fumante rojo es una cuesti\u00f3n de seguridad del proceso y corresponde a la primera conversaci\u00f3n, no a una nota al pie.<\/p>\n

Qu\u00e9 incluir en el pedido<\/h2>\n
\n\n\n\n\n\n\n\n\n\n
L\u00ednea del pedido<\/th>\nQu\u00e9 indicar<\/th>\n<\/tr>\n<\/thead>\n
Calidad y norma<\/td>\nGrade 2 (UNS R50400) seg\u00fan ASTM B265 para chapa gruesa o ASTM B338 para tubo cubre la mayor\u00eda de los servicios con \u00e1cido n\u00edtrico. Grade 12 (UNS R53400) cuando predomina la banda de ebullici\u00f3n de concentraci\u00f3n intermedia. Vapor sin condensaci\u00f3n: Grade 7 (UNS R52400). \u00c1cido caliente muy puro y servicio de condensaci\u00f3n donde preocupa el ataque a las uniones soldadas: Grade 1 (UNS R50250). Cuando se dan ambas condiciones, Grade 11 (UNS R52250) es Grade 1 con adici\u00f3n de paladio<\/td>\n<\/tr>\n
Datos de servicio<\/td>\nIntervalo de concentraci\u00f3n en porcentaje en peso, no solo el m\u00e1ximo; temperatura; si la superficie est\u00e1 calentada; l\u00edquido, vapor o condensaci\u00f3n; recirculaci\u00f3n o paso \u00fanico<\/td>\n<\/tr>\n
Contaminantes<\/td>\nFluoruros, cloruros y cualquier ion met\u00e1lico ya presente en la corriente<\/td>\n<\/tr>\n
Requisitos de soldadura<\/td>\nCalidad del material de aporte y cualquier examen de soldadura, porque las uniones soldadas son el elemento expuesto en \u00e1cido puro caliente<\/td>\n<\/tr>\n
Certificado<\/td>\nEN 10204 tipo 3.1 con n\u00fameros de colada y de vertido<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Una observaci\u00f3n de la preparaci\u00f3n de ofertas para este trabajo: la pregunta que cambia la respuesta con m\u00e1s frecuencia no es la concentraci\u00f3n del \u00e1cido, sino si la superficie mojada est\u00e1 calentada. Una superficie calefactora con \u00e1cido al 90 por ciento en ebullici\u00f3n y una l\u00ednea de l\u00edquido a granel a la misma concentraci\u00f3n son servicios diferentes y pueden acabar requiriendo calidades diferentes.<\/p>\n

Detalles de especificaci\u00f3n con fuentes<\/h2>\n

Los valores de corrosi\u00f3n anteriores proceden del manual publicado de resistencia a la corrosi\u00f3n del titanio de TIMET (Titanium Metals Corporation): corrosi\u00f3n de superficies calefactoras de titanio y acero inoxidable en \u00e1cido n\u00edtrico al 90 por ciento en ebullici\u00f3n a 240, 275 y 310 F; efecto del cromo sobre la corrosi\u00f3n en \u00e1cido al 68 por ciento en ebullici\u00f3n durante tres periodos de 48 horas; efecto del titanio disuelto en ensayos de 24 horas al 40 y al 68 por ciento; resistencia a vapores de \u00e1cido n\u00edtrico durante una exposici\u00f3n de 144 horas sobre el aze\u00f3tropo al 70 por ciento en ebullici\u00f3n; la curva de concentraci\u00f3n en ebullici\u00f3n para las tres calidades; el ensayo de agua regia en ebullici\u00f3n de 96 horas; y la advertencia sobre \u00e1cido n\u00edtrico fumante rojo. Las identidades de las calidades corresponden a ASTM: Grade 2 bajo UNS R50400, Grade 7 bajo UNS R52400 con paladio del 0.12 al 0.25 por ciento, y Grade 12 bajo UNS R53400 con molibdeno del 0.2 al 0.4 por ciento y n\u00edquel del 0.6 al 0.9 por ciento.<\/p>\n

Nota de alcance sobre la aplicabilidad de estas cifras: cada fila es un ensayo espec\u00edfico, no una predicci\u00f3n de servicio. Las filas de superficie calefactora corresponden a una concentraci\u00f3n y tres temperaturas del metal; las de contaminaci\u00f3n son periodos de 48 horas con sustituci\u00f3n del \u00e1cido en cada periodo; las de titanio disuelto son de 24 horas; las de vapor son de 144 horas sobre un aze\u00f3tropo. Los ensayos breves en \u00e1cido nuevo tienden a dar resultados peores que un circuito de funcionamiento equilibrado, que es exactamente lo que demuestra la tabla de titanio disuelto. Util\u00edcelos para comparar calidades y conocer los l\u00edmites estrictos, y despu\u00e9s confirme su propio servicio con los datos reales de la corriente. Beiyu Titanium suministra la chapa gruesa, el tubo y la barra seg\u00fan las normas indicadas anteriormente con un certificado de inspecci\u00f3n 3.1 seg\u00fan EN 10204 conforme al alcance del pedido; los datos de corrosi\u00f3n son datos de ensayos publicados por terceros, no resultados de ensayos de Beiyu.<\/p>\n

Preguntas frecuentes<\/h2>\n

\u00bfQu\u00e9 calidad de titanio elegir para servicio con \u00e1cido n\u00edtrico?<\/strong> El titanio sin alear Grade 2 cubre la mayor parte del intervalo. Grade 12 es la calidad cuya curva de ebullici\u00f3n publicada se mantiene m\u00e1s baja cuando el servicio se sit\u00faa en la banda de concentraci\u00f3n intermedia. El vapor y el condensado requieren dos decisiones distintas, y la fuente las responde con dos tipos de evidencia diferentes. Para el vapor sin condensaci\u00f3n, rige la velocidad de corrosi\u00f3n del metal base y, en el ensayo de vapor de 144 horas de TIMET, Grade 7 (UNS R52400), con paladio, registr\u00f3 0.08 mpy frente a 0.8 de Grade 12 (UNS R53400) y 2.0 del titanio sin alear. Para \u00e1cido muy puro caliente y servicio con condensaci\u00f3n, la preocupaci\u00f3n no es el metal base, sino el ataque acelerado en las zonas soldadas; en ese caso, la preferencia publicada es Grade 1 (UNS R50250), sin alear y de mayor pureza. Cuando una corriente re\u00fane ambas condiciones, Grade 11 (UNS R52250) es Grade 1 con la misma adici\u00f3n de paladio; Grades 16 y 17 son las opciones con menor contenido de paladio.<\/p>\n

\u00bfUn \u00e1cido m\u00e1s concentrado es siempre peor?<\/strong> No, y esta es la suposici\u00f3n err\u00f3nea m\u00e1s habitual en este servicio. En \u00e1cido n\u00edtrico en ebullici\u00f3n, la curva de TIMET alcanza un m\u00e1ximo alrededor del 40 al 50 por ciento para las calidades sin alear y con paladio, y desciende hacia el 70 por ciento, por lo que una corriente de concentraci\u00f3n intermedia puede representar un servicio m\u00e1s exigente que una concentrada.<\/p>\n

\u00bfPuede utilizarse titanio en \u00e1cido n\u00edtrico fumante rojo?<\/strong> No. Las recomendaciones publicadas lo descartan por el riesgo de reacci\u00f3n pirof\u00f3rica. Tr\u00e1telo como una exclusi\u00f3n por seguridad del proceso.<\/p>\n

\u00bfPor qu\u00e9 mi probeta de laboratorio dio peores resultados que la planta?<\/strong> Muy probablemente por el efecto del titanio disuelto. En los ensayos de 24 horas de TIMET, pasar de 0 a 40 mg\/l de ion titanio redujo la velocidad de corrosi\u00f3n en \u00e1cido al 68 por ciento de 31.8 mpy a 0.4 mpy. El \u00e1cido fresco en un ensayo corto no presenta esa inhibici\u00f3n.<\/p>\n

\u00bfQu\u00e9 ocurre con los \u00e1cidos reductores, como el clorh\u00eddrico o el sulf\u00farico?<\/strong> Es el caso opuesto y requiere una calidad diferente. Consulte titanio Grade 7 en \u00e1cidos reductores<\/a>.<\/p>\n

\u00bfQu\u00e9 norma se aplica al material?<\/strong> La chapa gruesa y la chapa fina se ajustan a ASTM B265, el tubo a ASTM B338 y la barra a ASTM B348. La gu\u00eda de chapa gruesa est\u00e1 en la gu\u00eda de chapa fina y chapa gruesa ASTM B265<\/a>.<\/p>\n

Env\u00ede los datos de la corriente con la solicitud de oferta<\/h2>\n

Env\u00ede el intervalo de concentraci\u00f3n del \u00e1cido, la temperatura, si la superficie se calienta, la fase l\u00edquida o vapor, la recirculaci\u00f3n, los contaminantes y la calidad, norma, dimensiones y cantidad a la p\u00e1gina de solicitud de oferta de Beiyu<\/a>. Revisado por Penn Ma<\/a>, 15 a\u00f1os en la exportaci\u00f3n de productos de titanio de f\u00e1brica. \u00daltima revisi\u00f3n: 2026-09-02.<\/p>","protected":false},"excerpt":{"rendered":"

In boiling 90 percent nitric acid on a heating surface, the tests published by TIMET put unalloyed titanium at 1.0 to 6.6 mpy (0.03 to 0.17 mm\/y) while Type 304L stainless ran 150 to 2,900 mpy (3.8 to 73.7 mm\/y) in the same TIMET tests. That two-to-three order of magnitude gap is why nitric acid […]<\/p>\n","protected":false},"author":2,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_templately_pack_id":"","_templately_imported_at":"","_templately_source":"","_templately_import_session_id":"","site-sidebar-layout":"default","site-content-layout":"","ast-site-content-layout":"default","site-content-style":"default","site-sidebar-style":"default","ast-global-header-display":"","ast-banner-title-visibility":"","ast-main-header-display":"","ast-hfb-above-header-display":"","ast-hfb-below-header-display":"","ast-hfb-mobile-header-display":"","site-post-title":"","ast-breadcrumbs-content":"","ast-featured-img":"","footer-sml-layout":"","ast-disable-related-posts":"","theme-transparent-header-meta":"","adv-header-id-meta":"","stick-header-meta":"","header-above-stick-meta":"","header-main-stick-meta":"","header-below-stick-meta":"","astra-migrate-meta-layouts":"default","ast-page-background-enabled":"default","ast-page-background-meta":{"desktop":{"background-color":"var(--ast-global-color-5)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"ast-content-background-meta":{"desktop":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"footnotes":""},"categories":[27,137],"tags":[],"class_list":["post-6032","post","type-post","status-publish","format-standard","hentry","category-news","category-technical-guides"],"yoast_head":"\nTitanium in Nitric Acid: Rates and Hard Limits | Beiyu<\/title>\n<meta name=\"description\" content=\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\" \/>\n<meta name=\"robots\" content=\"index, follow, max-snippet:-1, max-image-preview:large, max-video-preview:-1\" \/>\n<link rel=\"canonical\" href=\"https:\/\/beiyutitanium.com\/es\/titanium-in-nitric-acid\/\" \/>\n<meta property=\"og:locale\" content=\"es_ES\" \/>\n<meta property=\"og:type\" content=\"article\" \/>\n<meta property=\"og:title\" content=\"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu\" \/>\n<meta property=\"og:description\" content=\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\" \/>\n<meta property=\"og:url\" content=\"https:\/\/beiyutitanium.com\/es\/titanium-in-nitric-acid\/\" \/>\n<meta property=\"og:site_name\" content=\"Beiyu Titanium\" \/>\n<meta property=\"article:published_time\" content=\"2026-09-02T23:10:00+00:00\" \/>\n<meta property=\"article:modified_time\" content=\"2026-09-02T23:55:10+00:00\" \/>\n<meta property=\"og:image\" content=\"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/06\/grade-12-titanium-weld-neck-flange-astm-b381-asme-b16-5-scaled.jpg\" \/>\n\t<meta property=\"og:image:width\" content=\"1200\" \/>\n\t<meta property=\"og:image:height\" content=\"999\" \/>\n\t<meta property=\"og:image:type\" content=\"image\/jpeg\" \/>\n<meta name=\"author\" content=\"Penn Ma\" \/>\n<meta name=\"twitter:card\" content=\"summary_large_image\" \/>\n<meta name=\"twitter:label1\" content=\"Written by\" \/>\n\t<meta name=\"twitter:data1\" content=\"Penn Ma\" \/>\n\t<meta name=\"twitter:label2\" content=\"Est. reading time\" \/>\n\t<meta name=\"twitter:data2\" content=\"11 minutes\" \/>\n<script type=\"application\/ld+json\" class=\"yoast-schema-graph\">{\"@context\":\"https:\\\/\\\/schema.org\",\"@graph\":[{\"@type\":\"Article\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#article\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"},\"author\":{\"name\":\"Penn Ma\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/person\\\/3560db17cf08813edf34f012735b971b\"},\"headline\":\"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits\",\"datePublished\":\"2026-09-02T23:10:00+00:00\",\"dateModified\":\"2026-09-02T23:55:10+00:00\",\"mainEntityOfPage\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"},\"wordCount\":2327,\"publisher\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\"},\"articleSection\":[\"News\",\"Technical Guides\"],\"inLanguage\":\"es-ES\"},{\"@type\":\"WebPage\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\",\"name\":\"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#website\"},\"datePublished\":\"2026-09-02T23:10:00+00:00\",\"dateModified\":\"2026-09-02T23:55:10+00:00\",\"description\":\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\",\"breadcrumb\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#breadcrumb\"},\"inLanguage\":\"es-ES\",\"potentialAction\":[{\"@type\":\"ReadAction\",\"target\":[\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"]}]},{\"@type\":\"BreadcrumbList\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#breadcrumb\",\"itemListElement\":[{\"@type\":\"ListItem\",\"position\":1,\"name\":\"Home\",\"item\":\"https:\\\/\\\/beiyutitanium.com\\\/\"},{\"@type\":\"ListItem\",\"position\":2,\"name\":\"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits\"}]},{\"@type\":\"WebSite\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#website\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/\",\"name\":\"Beiyu Titanium\",\"description\":\"Certified titanium materials and custom components for aerospace, medical, chemical, and industrial applications.\",\"publisher\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\"},\"potentialAction\":[{\"@type\":\"SearchAction\",\"target\":{\"@type\":\"EntryPoint\",\"urlTemplate\":\"https:\\\/\\\/beiyutitanium.com\\\/?s={search_term_string}\"},\"query-input\":{\"@type\":\"PropertyValueSpecification\",\"valueRequired\":true,\"valueName\":\"search_term_string\"}}],\"inLanguage\":\"es-ES\"},{\"@type\":\"Organization\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\",\"name\":\"Beiyu Titanium\",\"alternateName\":\"\u5317\u9a6d\u949b\u4e1a\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/\",\"logo\":{\"@type\":\"ImageObject\",\"inLanguage\":\"es-ES\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/logo\\\/image\\\/\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/wp-content\\\/uploads\\\/2026\\\/03\\\/logo4.png\",\"contentUrl\":\"https:\\\/\\\/beiyutitanium.com\\\/wp-content\\\/uploads\\\/2026\\\/03\\\/logo4.png\",\"width\":429,\"height\":116,\"caption\":\"Beiyu Titanium\"},\"image\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/logo\\\/image\\\/\"},\"sameAs\":[\"https:\\\/\\\/www.linkedin.com\\\/company\\\/113015050\\\/\",\"https:\\\/\\\/www.youtube.com\\\/channel\\\/UC4Rr5qjUmKbbnROzU8zwluQ\",\"https:\\\/\\\/www.instagram.com\\\/beiyutrade\\\/\",\"https:\\\/\\\/www.facebook.com\\\/people\\\/Beiyu-Titanium-Group\\\/61580787646046\\\/\",\"https:\\\/\\\/www.crunchbase.com\\\/organization\\\/beiyu-titanium\",\"https:\\\/\\\/www.wikidata.org\\\/wiki\\\/Q140386451\"],\"contactPoint\":{\"@type\":\"ContactPoint\",\"contactType\":\"sales\",\"email\":\"penn@beiyutitanium.com\",\"availableLanguage\":[\"English\",\"Chinese\"]},\"description\":\"Beiyu Titanium (legal entity Jiaxing Beiyu New Materials Technology Co., Ltd.) is a China-based supplier and exporter of ASTM and AMS titanium bar, plate, sheet, tube, pipe, forgings, flanges, fasteners and custom machined parts, plus nickel and Inconel alloys, for chemical, marine, medical and industrial buyers worldwide. Production runs through the Beiyu titanium mill in Baoji, Shaanxi. Orders are RFQ-based, with EN 10204 3.1 mill test certificates and heat-number traceability available on request.\",\"areaServed\":\"Worldwide\",\"knowsAbout\":[\"Titanium\",\"Titanium alloy\",\"Titanium bar\",\"Titanium sheet and plate\",\"Titanium tube and pipe\",\"Titanium forgings\",\"Titanium wire\",\"Titanium anode\"],\"address\":{\"@type\":\"PostalAddress\",\"streetAddress\":\"Baotai Road Industrial Park, High-tech Development Zone\",\"addressLocality\":\"Baoji\",\"addressRegion\":\"Shaanxi\",\"addressCountry\":\"CN\"},\"legalName\":\"Jiaxing Beiyu New Materials Technology Co., Ltd.\"},{\"@type\":\"Person\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/person\\\/3560db17cf08813edf34f012735b971b\",\"name\":\"Penn Ma\",\"image\":{\"@type\":\"ImageObject\",\"inLanguage\":\"es-ES\",\"@id\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"url\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"contentUrl\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"caption\":\"Penn Ma\"},\"description\":\"Penn Ma is the person who answers the RFQs at Beiyu Titanium. Over 15 years in titanium export he has learned to review each specification line himself, checking grade, standard, dimensions, tolerance and certificate scope against mill capability before quoting, rather than routing enquiries through a sales desk. He came to titanium supply from the other side of the transaction. Before leading Beiyu's international business he worked at Koch (Koch-Glitsch) and was directly involved in delivering a SABIC petrochemical project in Fujian, China. That work was built on inspection and test plans, material certification and heat traceability, third party inspection coordination, and project documentation and dossier control. Those are the same four things a process industry or regulated buyer will hold a titanium supplier to, and having had to enforce them as a customer is why they are treated here as part of the supply rather than as paperwork produced afterwards. His day-to-day work spans the questions this site is written to answer: choosing between commercially pure and alloyed titanium grades for a corrosive service, reading a mill test certificate against the ordered standard, and matching a buyer's designation (ASTM grade, UNS, German Werkstoff number or French NF code) to the same metal across markets. Beiyu supplies titanium, nickel-alloy and refractory mill products across bar, rod, plate, tube, block, ring, coil, ingot, forgings and machined parts, with EN 10204 3.1 documentation and heat-number traceability.\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/es\\\/author\\\/penn-ma\\\/\"}]}<\/script>\n<!-- \/ Yoast SEO plugin. -->","yoast_head_json":{"title":"Titanio en \u00e1cido n\u00edtrico: velocidades y l\u00edmites estrictos | Beiyu","description":"Velocidades de corrosi\u00f3n publicadas para titanio en \u00e1cido n\u00edtrico: el pico de concentraci\u00f3n intermedia, por qu\u00e9 inhiben los iones met\u00e1licos disueltos, la fase de vapor y el intervalo de composici\u00f3n fumante rojo.","robots":{"index":"index","follow":"follow","max-snippet":"max-snippet:-1","max-image-preview":"max-image-preview:large","max-video-preview":"max-video-preview:-1"},"canonical":"https:\/\/beiyutitanium.com\/es\/titanium-in-nitric-acid\/","og_locale":"es_ES","og_type":"article","og_title":"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu","og_description":"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.","og_url":"https:\/\/beiyutitanium.com\/es\/titanium-in-nitric-acid\/","og_site_name":"Beiyu Titanium","article_published_time":"2026-09-02T23:10:00+00:00","article_modified_time":"2026-09-02T23:55:10+00:00","og_image":[{"width":1200,"height":999,"url":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/06\/grade-12-titanium-weld-neck-flange-astm-b381-asme-b16-5-scaled.jpg","type":"image\/jpeg"}],"author":"Penn Ma","twitter_card":"summary_large_image","twitter_misc":{"Written by":"Penn Ma","Est. reading time":"11 minutes"},"schema":{"@context":"https:\/\/schema.org","@graph":[{"@type":"Article","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#article","isPartOf":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"},"author":{"name":"Penn Ma","@id":"https:\/\/beiyutitanium.com\/#\/schema\/person\/3560db17cf08813edf34f012735b971b"},"headline":"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits","datePublished":"2026-09-02T23:10:00+00:00","dateModified":"2026-09-02T23:55:10+00:00","mainEntityOfPage":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"},"wordCount":2327,"publisher":{"@id":"https:\/\/beiyutitanium.com\/#organization"},"articleSection":["News","Technical Guides"],"inLanguage":"es-ES"},{"@type":"WebPage","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/","url":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/","name":"Titanio en \u00e1cido n\u00edtrico: velocidades y l\u00edmites estrictos | Beiyu","isPartOf":{"@id":"https:\/\/beiyutitanium.com\/#website"},"datePublished":"2026-09-02T23:10:00+00:00","dateModified":"2026-09-02T23:55:10+00:00","description":"Velocidades de corrosi\u00f3n publicadas para titanio en \u00e1cido n\u00edtrico: el pico de concentraci\u00f3n intermedia, por qu\u00e9 inhiben los iones met\u00e1licos disueltos, la fase de vapor y el intervalo de composici\u00f3n fumante rojo.","breadcrumb":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#breadcrumb"},"inLanguage":"es-ES","potentialAction":[{"@type":"ReadAction","target":["https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"]}]},{"@type":"BreadcrumbList","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#breadcrumb","itemListElement":[{"@type":"ListItem","position":1,"name":"Home","item":"https:\/\/beiyutitanium.com\/"},{"@type":"ListItem","position":2,"name":"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits"}]},{"@type":"WebSite","@id":"https:\/\/beiyutitanium.com\/#website","url":"https:\/\/beiyutitanium.com\/","name":"Beiyu Titanium","description":"Materiales de titanio certificados y componentes personalizados para aplicaciones aeroespaciales, m\u00e9dicas, qu\u00edmicas e industriales.","publisher":{"@id":"https:\/\/beiyutitanium.com\/#organization"},"potentialAction":[{"@type":"SearchAction","target":{"@type":"EntryPoint","urlTemplate":"https:\/\/beiyutitanium.com\/?s={search_term_string}"},"query-input":{"@type":"PropertyValueSpecification","valueRequired":true,"valueName":"search_term_string"}}],"inLanguage":"es-ES"},{"@type":"Organization","@id":"https:\/\/beiyutitanium.com\/#organization","name":"Beiyu Titanium","alternateName":"\u5317\u9a6d\u949b\u4e1a","url":"https:\/\/beiyutitanium.com\/","logo":{"@type":"ImageObject","inLanguage":"es-ES","@id":"https:\/\/beiyutitanium.com\/#\/schema\/logo\/image\/","url":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/03\/logo4.png","contentUrl":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/03\/logo4.png","width":429,"height":116,"caption":"Beiyu Titanium"},"image":{"@id":"https:\/\/beiyutitanium.com\/#\/schema\/logo\/image\/"},"sameAs":["https:\/\/www.linkedin.com\/company\/113015050\/","https:\/\/www.youtube.com\/channel\/UC4Rr5qjUmKbbnROzU8zwluQ","https:\/\/www.instagram.com\/beiyutrade\/","https:\/\/www.facebook.com\/people\/Beiyu-Titanium-Group\/61580787646046\/","https:\/\/www.crunchbase.com\/organization\/beiyu-titanium","https:\/\/www.wikidata.org\/wiki\/Q140386451"],"contactPoint":{"@type":"ContactPoint","contactType":"sales","email":"penn@beiyutitanium.com","availableLanguage":["English","Chinese"]},"description":"Beiyu Titanium (entidad jur\u00eddica Jiaxing Beiyu New Materials Technology Co., Ltd.) es un proveedor y exportador con sede en China de barras, chapa gruesa, chapa fina, tubos, tuber\u00edas, piezas forjadas, bridas, elementos de fijaci\u00f3n y piezas mecanizadas a medida de titanio seg\u00fan ASTM y AMS, adem\u00e1s de aleaciones de n\u00edquel e Inconel, para compradores de los sectores qu\u00edmico, marino, m\u00e9dico e industrial de todo el mundo. La producci\u00f3n se realiza en la f\u00e1brica de titanio de Beiyu en Baoji, Shaanxi. Los pedidos se basan en solicitudes de oferta, con certificados de inspecci\u00f3n 3.1 seg\u00fan EN 10204 y trazabilidad por n\u00famero de colada disponibles a petici\u00f3n.","areaServed":"Worldwide","knowsAbout":["Titanium","Titanium alloy","Titanium bar","Titanium sheet and plate","Titanium tube and pipe","Titanium forgings","Titanium wire","Titanium anode"],"address":{"@type":"PostalAddress","streetAddress":"Baotai Road Industrial Park, High-tech Development Zone","addressLocality":"Baoji","addressRegion":"Shaanxi","addressCountry":"CN"},"legalName":"Jiaxing Beiyu New Materials Technology Co., Ltd."},{"@type":"Person","@id":"https:\/\/beiyutitanium.com\/#\/schema\/person\/3560db17cf08813edf34f012735b971b","name":"Penn Ma","image":{"@type":"ImageObject","inLanguage":"es-ES","@id":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","url":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","contentUrl":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","caption":"Penn Ma"},"description":"Penn Ma es la persona que responde a las solicitudes de oferta en Beiyu Titanium. Durante m\u00e1s de 15 a\u00f1os de exportaci\u00f3n de titanio, ha aprendido a revisar personalmente cada l\u00ednea de especificaci\u00f3n, comprobando calidad, norma, dimensiones, tolerancia y alcance del certificado frente a la capacidad de la f\u00e1brica antes de emitir una oferta, en lugar de canalizar las consultas a trav\u00e9s de un departamento comercial. Lleg\u00f3 al suministro de titanio desde el otro lado de la transacci\u00f3n. Antes de dirigir el negocio internacional de Beiyu, trabaj\u00f3 en Koch (Koch-Glitsch) y particip\u00f3 directamente en la entrega de un proyecto petroqu\u00edmico de SABIC en Fujian, China. Ese trabajo se basaba en planes de inspecci\u00f3n y ensayo, certificaci\u00f3n de materiales y trazabilidad por n\u00famero de colada, coordinaci\u00f3n de inspecci\u00f3n por tercera parte y control de la documentaci\u00f3n y los expedientes del proyecto. Esas son las mismas cuatro cosas que un comprador de la industria de procesos o regulada exigir\u00e1 a un proveedor de titanio, y haber tenido que aplicarlas como cliente es la raz\u00f3n por la que aqu\u00ed se tratan como parte del suministro y no como documentaci\u00f3n elaborada posteriormente. Su trabajo diario abarca las cuestiones que este sitio est\u00e1 concebido para responder: elegir entre calidades de titanio comercialmente puro y aleado para un servicio corrosivo, interpretar un certificado de materiales frente a la norma solicitada y relacionar la designaci\u00f3n de un comprador (calidad ASTM, UNS, n\u00famero Werkstoff alem\u00e1n o c\u00f3digo NF franc\u00e9s) con el mismo metal en distintos mercados. Beiyu suministra productos de f\u00e1brica de titanio, aleaciones de n\u00edquel y materiales refractarios en barra, varilla, chapa gruesa, tubo, bloque, anillo, bobina, lingote, piezas forjadas y piezas mecanizadas, con documentaci\u00f3n EN 10204 3.1 y trazabilidad por n\u00famero de colada.","url":"https:\/\/beiyutitanium.com\/es\/author\/penn-ma\/"}]}},"_links":{"self":[{"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/posts\/6032","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/comments?post=6032"}],"version-history":[{"count":1,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/posts\/6032\/revisions"}],"predecessor-version":[{"id":6033,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/posts\/6032\/revisions\/6033"}],"wp:attachment":[{"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/media?parent=6032"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/categories?post=6032"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/beiyutitanium.com\/es\/wp-json\/wp\/v2\/tags?post=6032"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}