{"id":6032,"date":"2026-09-02T23:10:00","date_gmt":"2026-09-02T23:10:00","guid":{"rendered":"https:\/\/beiyutitanium.com\/?p=6032"},"modified":"2026-09-02T23:55:10","modified_gmt":"2026-09-02T23:55:10","slug":"titanium-in-nitric-acid","status":"publish","type":"post","link":"https:\/\/beiyutitanium.com\/fr\/titanium-in-nitric-acid\/","title":{"rendered":"Titane dans l'acide nitrique : vitesses, pic \u00e0 mi-concentration et limites absolues"},"content":{"rendered":"

Dans de l'acide nitrique \u00e0 90 pour cent en \u00e9bullition sur une surface chauffante, les essais publi\u00e9s par TIMET placent le titane non alli\u00e9 entre 1.0 et 6.6 mpy (0.03 \u00e0 0.17 mm\/y), tandis que l'acier inoxydable Type 304L se situait entre 150 et 2900 mpy (3.8 \u00e0 73.7 mm\/y) dans les m\u00eames essais TIMET. Cet \u00e9cart de deux \u00e0 trois ordres de grandeur explique pourquoi le service \u00e0 l'acide nitrique constitue l'un des cas les plus favorables au titane. Mais les m\u00eames donn\u00e9es montrent deux points qu'un concepteur doit conna\u00eetre : la vitesse de corrosion atteint son maximum au milieu de la plage de concentration plut\u00f4t qu'\u00e0 son sommet, et l'acide nitrique rouge fumant constitue une exclusion stricte.<\/p>\n

Titane par rapport \u00e0 l'acier inoxydable sur une surface chauffante<\/h2>\n
\n\n\n\n\n\n\n\n
Corrosion des surfaces chauffantes en titane et en acier inoxydable expos\u00e9es \u00e0 de l'acide nitrique \u00e0 90 pour cent bouillant \u00e0 215 F, selon le manuel publi\u00e9 par TIMET sur la r\u00e9sistance \u00e0 la corrosion du titane. Les temp\u00e9ratures du m\u00e9tal sont celles de la surface chauff\u00e9e, et non celles de l'acide en vrac.<\/caption>\n
Temp\u00e9rature du m\u00e9tal<\/th>\ntitane non alli\u00e9<\/th>\nAcier inoxydable Type 304L<\/th>\n<\/tr>\n<\/thead>\n
240 F (116 C)<\/td>\n1.1 \u00e0 6.6 mpy (0.03 \u00e0 0.17 mm\/y)<\/td>\n150 \u00e0 518 mpy (3.8 \u00e0 13.2 mm\/y)<\/td>\n<\/tr>\n
275 F (135 C)<\/td>\n1.6 \u00e0 6.1 mpy (0.04 \u00e0 0.15 mm\/y)<\/td>\n676 \u00e0 2900 mpy (17.2 \u00e0 73.7 mm\/y)<\/td>\n<\/tr>\n
310 F (154 C)<\/td>\n1.0 \u00e0 2.3 mpy (0.03 \u00e0 0.06 mm\/y)<\/td>\n722 \u00e0 2900 mpy (18.3 \u00e0 73.7 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

La colonne relative \u00e0 l'acier inoxydable explique pourquoi l'\u00e9quipement est sp\u00e9cifi\u00e9 en titane. Cette comparaison pr\u00e9sente deux limites objectives. Type 304L n'est pas ce qu'une usine d'acide nitrique sp\u00e9cifierait r\u00e9ellement \u00e0 cette temp\u00e9rature : les v\u00e9ritables concurrents sont les aust\u00e9nitiques contenant du silicium tels que UNS S30600, et au-dessus d'environ 80 pour cent d'acide, l'aluminium. La colonne relative au titane doit \u00e9galement \u00eatre interpr\u00e9t\u00e9e pour ce qu'elle est : une condition de surface chauffante, bouillante, \u00e0 une concentration donn\u00e9e, plus s\u00e9v\u00e8re qu'un service en liquide en vrac \u00e0 la m\u00eame temp\u00e9rature.<\/p>\n

La partie contre-intuitive : la pire concentration se situe au milieu<\/h2>\n

Les ing\u00e9nieurs d\u00e9couvrant le titane supposent souvent qu'un acide plus fort entra\u00eene une attaque plus rapide. Dans de l'acide nitrique pur bouillant, en phase liquide, la courbe publi\u00e9e montre l'inverse. La vitesse de corrosion augmente \u00e0 partir d'une valeur proche de z\u00e9ro \u00e0 10 pour cent, puis diminue de nouveau vers 70 pour cent, avec un pic entre les deux. Sur la courbe TIMET, les nuances non alli\u00e9es et contenant du palladium culminent pr\u00e8s de 24 \u00e0 26 mpy (0.61 \u00e0 0.66 mm\/y) quelque part autour de 40 \u00e0 50 pour cent en poids, tandis que Grade 12 culmine plus t\u00f4t et \u00e0 un niveau plus faible, pr\u00e8s de 15 mpy (0.38 mm\/y), et reste plus faible sur toute la plage interm\u00e9diaire.<\/p>\n

La cons\u00e9quence pratique : sur cette courbe d'acide pur bouillant, une colonne ou un rebouilleur fonctionnant toute sa dur\u00e9e de vie \u00e0 35 pour cent d'acide est soumis \u00e0 un service plus s\u00e9v\u00e8re qu'un autre \u00e0 65 pour cent, et un proc\u00e9d\u00e9 qui traverse la bande interm\u00e9diaire est plus s\u00e9v\u00e8re que l'un ou l'autre. Indiquez la plage de concentration, et non seulement le maximum.<\/p>\n

Le chiffre \u00e0 utiliser pour dimensionner l'\u00e9paisseur de paroi<\/h2>\n

Avant d'aller plus loin, il convient d'indiquer clairement ce sur quoi les donn\u00e9es publi\u00e9es concordent ou non, car cette page pr\u00e9sente deux chiffres pour ce qui semble \u00eatre le m\u00eame service. Pour le titane non alli\u00e9 dans de l'acide bouillant \u00e0 environ 68 \u00e0 70 pour cent :<\/p>\n

\n\n\n\n\n\n\n
Source au sein du m\u00eame manuel<\/th>\nVitesse<\/th>\n<\/tr>\n<\/thead>\n
La courbe concentration-\u00e9bullition pour l'acide pur, lue \u00e0 70 pour cent. Liquide bouillant, \u00e9prouvette non chauff\u00e9e ; dur\u00e9e d'exposition non indiqu\u00e9e dans la source cit\u00e9e<\/td>\nEnviron 5 mpy (0,13 mm\/y)<\/td>\n<\/tr>\n
Le tableau du titane dissous, liquide bouillant \u00e0 68 pour cent sans ion titane pr\u00e9sent, essai de 24 heures<\/td>\n31.8 mpy (0.81 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Il s'agit de r\u00e9f\u00e9rences d'essais diff\u00e9rentes, et l'\u00e9cart n'est une erreur dans aucune des deux. Il s'agit de la dispersion r\u00e9elle dans ce service, et les propres donn\u00e9es du manuel ailleurs placent l'acide \u00e0 70 pour cent en \u00e9bullition dans une plage d'environ 2.5 \u00e0 37 mpy (0.064 \u00e0 0.94 mm\/y), \u00e9galement sans dur\u00e9e d'exposition indiqu\u00e9e. La r\u00e8gle de conception qui en d\u00e9coule est la partie importante de cette page : dimensionner l'\u00e9paisseur de paroi selon le vitesse de corrosion en acide pur non inhib\u00e9, de l'ordre de 0,8 mm par an \u00e0 la concentration la plus d\u00e9favorable, et consid\u00e9rer l'inhibition par les ions m\u00e9talliques comme une marge plut\u00f4t que comme une base de conception.<\/strong> La raison est expos\u00e9e dans la section suivante : plusieurs emplacements dans une installation r\u00e9elle sont expos\u00e9s \u00e0 un acide ne contenant aucun ion inhibiteur.<\/p>\n

Les cations m\u00e9talliques dissous inhibent ; les autres contaminants ont l'effet inverse<\/h2>\n

L'effet est sp\u00e9cifique aux cations m\u00e9talliques dissous. Le manuel cite le silicium, le chrome, le fer, le titane et les ions de m\u00e9taux pr\u00e9cieux tels que le platine et le ruth\u00e9nium comme inhibiteurs \u00e0 l'\u00e9tat de traces. Il ne s'agit pas d'une r\u00e8gle g\u00e9n\u00e9rale relative \u00e0 la contamination : les sels contenant des chlorures n\u00e9cessitent leurs propres donn\u00e9es, tandis qu'une forte teneur en sels de nitrate fait \u00e9voluer le taux dans l'autre sens et produit les valeurs les plus d\u00e9favorables en acide nitrique pur indiqu\u00e9es dans le manuel. Dans cette limite, dans l'acide nitrique \u00e0 68 pour cent bouillant, une faible contamination au chrome a consid\u00e9rablement aggrav\u00e9 le comportement du Type 304L tandis que celui du titane s'est am\u00e9lior\u00e9 :<\/p>\n

\n\n\n\n\n\n\n\n\n\n
Effet du chrome sur la corrosion de l'acier inoxydable et du titane dans l'acide nitrique \u00e0 68 pour cent bouillant, trois p\u00e9riodes de 48 heures avec renouvellement de l'acide \u00e0 chaque p\u00e9riode, selon le manuel TIMET publi\u00e9.<\/caption>\n
Chrome en solution<\/th>\nType 304L recuit<\/th>\ntitane non alli\u00e9<\/th>\n<\/tr>\n<\/thead>\n
0,0 pour cent<\/td>\n12 \u00e0 18 mpy (0.30 \u00e0 0.46 mm\/y)<\/td>\n3.5 \u00e0 3.8 mpy (0.09 \u00e0 0.10 mm\/y)<\/td>\n<\/tr>\n
0,0005 pour cent<\/td>\n12 \u00e0 20 mpy (0.30 \u00e0 0.51 mm\/y)<\/td>\nNon rapport\u00e9<\/td>\n<\/tr>\n
0,005 pour cent<\/td>\n60 \u00e0 90 mpy (1.5 \u00e0 2.3 mm\/y)<\/td>\n0.9 \u00e0 1.6 mpy (0.022 \u00e0 0.041 mm\/y)<\/td>\n<\/tr>\n
0,05 pour cent<\/td>\n980 \u00e0 1600 mpy (24.9 \u00e0 40.6 mm\/y)<\/td>\nNon rapport\u00e9<\/td>\n<\/tr>\n
0,01 pour cent<\/td>\nNon rapport\u00e9<\/td>\n0.1 \u00e0 1.4 mpy (0.003 \u00e0 0.036 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Le titane dissous lui-m\u00eame est un inhibiteur encore plus puissant de la corrosion du titane dans ce service :<\/p>\n

\n\n\n\n\n\n\n\n\n\n
Effet du titane dissous sur le vitesse de corrosion du titane non alli\u00e9 dans l'acide nitrique bouillant, essais de 24 heures, selon le manuel TIMET publi\u00e9.<\/caption>\n
Ion titane ajout\u00e9<\/th>\nDans HNO3 \u00e0 40 pour cent<\/th>\nDans HNO3 \u00e0 68 pour cent<\/th>\n<\/tr>\n<\/thead>\n
0 mg\/l<\/td>\n29.5 mpy (0.75 mm\/y)<\/td>\n31.8 mpy (0.81 mm\/y)<\/td>\n<\/tr>\n
10 mg\/l<\/td>\nNon rapport\u00e9<\/td>\n0.8 mpy (0.02 mm\/y)<\/td>\n<\/tr>\n
20 mg\/l<\/td>\n8.6 mpy (0.22 mm\/y)<\/td>\n2.4 mpy (0.06 mm\/y)<\/td>\n<\/tr>\n
40 mg\/l<\/td>\n1.9 mpy (0.05 mm\/y)<\/td>\n0.4 mpy (0.01 mm\/y)<\/td>\n<\/tr>\n
80 mg\/l<\/td>\n0.8 mpy (0.02 mm\/y)<\/td>\n0.4 mpy (0.01 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Le manuel applique cela aux circuits de recirculation tels que les boucles de rebouilleur de colonne de stripping, o\u00f9 l'inhibition r\u00e9sulte de l'atteinte d'un niveau stable de titane dissous. Deux limites doivent \u00eatre associ\u00e9es \u00e0 cela. Premi\u00e8rement, l'atteinte de ce niveau n'est pas automatique : elle d\u00e9pend de la surface mouill\u00e9e, du vitesse de corrosion, du volume de la boucle et du d\u00e9bit d'appoint, et l'effet s'autor\u00e9gule, car \u00e0 0.4 mpy le m\u00e9tal lib\u00e8re beaucoup moins de titane qu'\u00e0 31.8 mpy. Une boucle \u00e0 fort d\u00e9bit d'appoint est plus proche d'un passage unique que ne le sugg\u00e8re le terme recirculant. Deuxi\u00e8mement, et cela est plus important pour la s\u00e9curit\u00e9, plusieurs parties d'une installation r\u00e9elle sont expos\u00e9es \u00e0 un acide ne contenant aucun ion inhibiteur : les tron\u00e7ons \u00e0 passage unique, le d\u00e9marrage, la p\u00e9riode suivant un remplacement d'acide ou un rin\u00e7age, et le condensat qui, par ce m\u00eame m\u00e9canisme, est l'acide le plus pur du syst\u00e8me. Compar\u00e9e \u00e0 une boucle de recirculation \u00e0 l'\u00e9quilibre, une \u00e9prouvette de laboratoire dans un acide frais non inhib\u00e9 peut indiquer une valeur plus d\u00e9favorable, et non meilleure. Les emplacements \u00e0 passage unique et transitoires \u00e9num\u00e9r\u00e9s ci-dessus peuvent ressembler \u00e0 ce cas non inhib\u00e9, raison pour laquelle la base de conception ci-dessus utilise le taux non inhib\u00e9.<\/p>\n

La phase vapeur repr\u00e9sente un service diff\u00e9rent de la phase liquide<\/h2>\n
\n\n\n\n\n\n\n\n
R\u00e9sistance du titane \u00e0 la corrosion par les vapeurs d'acide nitrique, \u00e9chantillons suspendus au-dessus d'un az\u00e9otrope \u00e0 70 pour cent bouillant, exposition de 144 heures, selon le manuel TIMET publi\u00e9.<\/caption>\n
Nuance<\/th>\nTaux de corrosion<\/th>\n<\/tr>\n<\/thead>\n
titane non alli\u00e9<\/td>\n2.0 mpy (0.051 mm\/y)<\/td>\n<\/tr>\n
Grade 12 (Ti-0.3Mo-0.8Ni)<\/td>\n0.8 mpy (0.020 mm\/y)<\/td>\n<\/tr>\n
Non alli\u00e9 contenant du palladium<\/td>\n0.08 mpy (0.002 mm\/y)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

L'acide en condensation et le condensat ruisselant constituent le point de d\u00e9faillance classique en service d'acide nitrique, et le classement des nuances dans ce cas n'est pas le m\u00eame que dans le liquide. Pour l'acide chaud tr\u00e8s pur et pour les conditions de condensation, la pr\u00e9f\u00e9rence publi\u00e9e va au Grade 1 non alli\u00e9 de plus haute puret\u00e9 (UNS R50250), et la raison tient au comportement des soudures plut\u00f4t qu'\u00e0 la vitesse du m\u00e9tal de base dans ce tableau. Noter \u00e9galement ce que ce tableau est et n'est pas : des coupons suspendus dans la vapeur au-dessus de l'az\u00e9otrope pendant 144 heures. Il ne s'agit pas d'un essai sous film de condensation, et le manuel n'attribue aucune vitesse au condensat ruisselant, o\u00f9 que ce soit.<\/p>\n

Cas o\u00f9 le titane est exclu d'embl\u00e9e<\/h2>\n
\n\n\n\n\n\n\n\n\n\n
\u00c9tat<\/th>\nStatut<\/th>\n<\/tr>\n<\/thead>\n
Acide nitrique rouge fumant<\/td>\nNe pas utiliser.<\/strong> Le m\u00e9canisme publi\u00e9 n'est pas une simple corrosion : l'attaque est intergranulaire et laisse un r\u00e9sidu de surface de titane m\u00e9tallique finement divis\u00e9, qui est hautement pyrophorique et peut d\u00e9toner en pr\u00e9sence d'un agent oxydant puissant. Le manuel indique la plage de composition n\u00e9cessaire au d\u00e9veloppement de la r\u00e9action : teneur en eau inf\u00e9rieure \u00e0 1,34 pour cent et NO2 sup\u00e9rieure \u00e0 6 pour cent, et il pr\u00e9sente une zone d'incertitude explicite entre les r\u00e9gions r\u00e9active et non r\u00e9active. Son annexe \u00e9value s\u00e9par\u00e9ment l'acide rouge fumant contenant moins d'environ 2 pour cent d'eau comme sensible \u00e0 l'inflammation ; cette exclusion couvre donc la zone d'incertitujusqu'\u00e0 cette limite d'environ 2 pour cent d'eau, et non uniquement les compositions inf\u00e9rieures \u00e0 1,34 pour cent. V\u00e9rifiez votre analyse par rapport \u00e0 cette plage plut\u00f4t qu'\u00e0 l'appellation, car un flux est rarement d\u00e9sign\u00e9 comme rouge fumant sur la fiche technique.<\/td>\n<\/tr>\n
Acide nitrique blanc fumant<\/td>\nAcceptable selon le m\u00eame manuel, \u00e0 environ 0.1 mpy \u00e0 temp\u00e9rature ambiante. Ne pas interpr\u00e9ter l'exclusion de l'acide rouge fumant comme couvrant tous les acides fumants.<\/td>\n<\/tr>\n
Acide nitrique contenant des chlorures, jusqu'\u00e0 l'eau r\u00e9gale<\/td>\nUn risque quantifi\u00e9, qui inverse la logique habituelle des nuances. Dans l'essai d'\u00e9bullition de 96 heures en eau r\u00e9gale d\u00e9crit dans le manuel, trois parts d'acide chlorhydrique pour une part d'acide nitrique, le titane non alli\u00e9 et la nuance au palladium ont tous deux atteint 44 mpy (1,12 mm\/y), tandis que le Grade 12 a atteint 24 mpy (0,61 mm\/y). La nuance au palladium n'offrait donc aucun avantage par rapport au titane non alli\u00e9, tandis que le Grade 12 \u00e9tait le plus bas des trois. \u00c0 temp\u00e9rature ambiante, le titane est pratiquement inerte face \u00e0 l'eau r\u00e9gale. Les taux augmentent dans les acides mixtes \u00e0 mesure que la part d'acide r\u00e9ducteur ou la temp\u00e9rature augmente.<\/td>\n<\/tr>\n
Acide nitrique contenant des fluorures<\/td>\nExamen requis. Les fluorures dans l'acide peuvent former de l'acide fluorhydrique, qui attaque rapidement le titane.<\/td>\n<\/tr>\n
Acide chaud tr\u00e8s pur et condensat de vapeur<\/td>\nAutoris\u00e9 mais sensible \u00e0 la nuance. Les vitesses augmentent, les soudures constituent l'\u00e9l\u00e9ment expos\u00e9, et les nuances non alli\u00e9es de plus haute puret\u00e9 sont la pr\u00e9f\u00e9rence publi\u00e9e.<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Une page de fournisseur qui ne r\u00e9pertorie que les lignes favorables n'est pas utilisable pour la conception. L'exclusion de l'acide rouge fumant, en particulier, rel\u00e8ve de la s\u00e9curit\u00e9 des proc\u00e9d\u00e9s et doit figurer dans la premi\u00e8re discussion, et non dans une note de bas de page.<\/p>\n

\u00c0 indiquer sur la commande<\/h2>\n
\n\n\n\n\n\n\n\n\n\n
Ligne de commande<\/th>\n\u00c0 indiquer<\/th>\n<\/tr>\n<\/thead>\n
Nuance et norme<\/td>\nGrade 2 (UNS R50400) selon ASTM B265 pour la plaque ou ASTM B338 pour le tube couvre la plupart des applications \u00e0 l'acide nitrique. Grade 12 (UNS R53400) lorsque la plage d'\u00e9bullition \u00e0 concentration interm\u00e9diaire est d\u00e9terminante. Vapeur sans condensation : Grade 7 (UNS R52400). Acide chaud tr\u00e8s pur et conditions de condensation lorsque l'attaque des soudures est pr\u00e9occupante : Grade 1 (UNS R50250). Lorsque les deux s'appliquent, Grade 11 (UNS R52250) est du Grade 1 avec l'ajout de palladium<\/td>\n<\/tr>\n
Donn\u00e9es de service<\/td>\nPlage de concentration en pourcentage massique, et non seulement le maximum ; temp\u00e9rature ; si la surface est chauff\u00e9e ; liquide, vapeur ou condensation ; recirculation ou passage unique<\/td>\n<\/tr>\n
Contaminants<\/td>\nFluorures, chlorures et tous ions m\u00e9talliques d\u00e9j\u00e0 pr\u00e9sents dans le flux<\/td>\n<\/tr>\n
Exigences de soudage<\/td>\nNuance du m\u00e9tal d'apport et tout contr\u00f4le de soudure, car les soudures constituent la partie expos\u00e9e dans l'acide pur chaud<\/td>\n<\/tr>\n
Certificat<\/td>\nEN 10204 type 3.1 avec num\u00e9ros de coul\u00e9e et de versement<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n

Une remarque issue de l'\u00e9tablissement d'offres pour ce travail : la question qui modifie le plus souvent la r\u00e9ponse n'est pas la concentration de l'acide, mais si la surface en contact avec le fluide est chauff\u00e9e. Une surface chauffante dans de l'acide bouillant \u00e0 90 pour cent et une conduite de liquide en vrac \u00e0 la m\u00eame concentration correspondent \u00e0 des conditions de service diff\u00e9rentes et peuvent aboutir \u00e0 des nuances diff\u00e9rentes.<\/p>\n

D\u00e9tails des sp\u00e9cifications avec sources<\/h2>\n

Les valeurs de corrosion ci-dessus proviennent du manuel publi\u00e9 de r\u00e9sistance \u00e0 la corrosion du titane de TIMET (Titanium Metals Corporation) : corrosion des surfaces chauffantes en titane et en acier inoxydable dans l'acide nitrique bouillant \u00e0 90 pour cent \u00e0 240, 275 et 310 F ; effet du chrome sur la corrosion dans l'acide bouillant \u00e0 68 pour cent sur trois p\u00e9riodes de 48 heures ; effet du titane dissous lors d'essais de 24 heures \u00e0 40 et 68 pour cent ; r\u00e9sistance aux vapeurs d'acide nitrique sur une exposition de 144 heures au-dessus de l'az\u00e9otrope bouillant \u00e0 70 pour cent ; courbe concentration-\u00e9bullition pour les trois nuances ; essai de 96 heures \u00e0 l'eau r\u00e9gale bouillante ; et mise en garde concernant l'acide nitrique rouge fumant. Les identit\u00e9s des nuances sont conformes \u00e0 ASTM : Grade 2 sous UNS R50400, Grade 7 sous UNS R52400 avec du palladium \u00e0 0.12 \u00e0 0.25 pour cent, et Grade 12 sous UNS R53400 avec du molybd\u00e8ne \u00e0 0.2 \u00e0 0.4 pour cent et du nickel \u00e0 0.6 \u00e0 0.9 pour cent.<\/p>\n

Note sur le champ d'application de ces valeurs : chaque ligne correspond \u00e0 un essai sp\u00e9cifique, et non \u00e0 une pr\u00e9vision de service. Les lignes relatives aux surfaces chauffantes concernent une concentration \u00e0 trois temp\u00e9ratures de m\u00e9tal ; les lignes relatives aux contaminants concernent des p\u00e9riodes de 48 heures avec remplacement de l'acide \u00e0 chaque p\u00e9riode ; les lignes relatives au titane dissous concernent 24 hours ; les lignes relatives aux vapeurs concernent 144 hours au-dessus d'un az\u00e9otrope. Les essais courts dans de l'acide neuf tendent \u00e0 donner des r\u00e9sultats plus d\u00e9favorables qu'une boucle de fonctionnement \u00e0 l'\u00e9quilibre, ce que d\u00e9montre pr\u00e9cis\u00e9ment le tableau du titane dissous. Utilisez ces donn\u00e9es pour classer les nuances et conna\u00eetre les limites strictes, puis confirmez vos propres conditions de service avec les donn\u00e9es r\u00e9elles du flux. Beiyu Titanium fournit la plaque, le tube et la barre selon les normes indiqu\u00e9es ci-dessus avec un certificat de r\u00e9ception 3.1 selon EN 10204 selon le p\u00e9rim\u00e8tre de la commande ; les donn\u00e9es de corrosion sont des donn\u00e9es d'essais publi\u00e9es par des tiers, et non des r\u00e9sultats d'essais de Beiyu.<\/p>\n

Questions fr\u00e9quemment pos\u00e9es<\/h2>\n

Quelle nuance de titane pour un service en acide nitrique ?<\/strong> Le Grade 2 non alli\u00e9 couvre la majeure partie de la plage. Grade 12 est la nuance dont la courbe d'\u00e9bullition publi\u00e9e reste la plus basse lorsque les conditions de service se situent dans la plage de concentrations interm\u00e9diaires. Les vapeurs et les condensats sont deux cas diff\u00e9rents, et la source y r\u00e9pond par deux types de preuves diff\u00e9rents. Pour les vapeurs non condensantes, la vitesse du m\u00e9tal de base est d\u00e9terminante, et dans l'essai de vapeur TIMET de 144 heures, le Grade 7 contenant du palladium (UNS R52400) a atteint 0.08 mpy contre 0.8 pour Grade 12 (UNS R53400) et 2.0 pour le mat\u00e9riau non alli\u00e9. Pour l'acide tr\u00e8s pur chaud et les conditions condensantes, la pr\u00e9occupation n'est pas le m\u00e9tal de base mais l'attaque acc\u00e9l\u00e9r\u00e9e des soudures, et la pr\u00e9f\u00e9rence publi\u00e9e est alors le Grade 1 non alli\u00e9 de plus grande puret\u00e9 (UNS R50250). Lorsqu'un flux pr\u00e9sente les deux cas, Grade 11 (UNS R52250) est du Grade 1 avec la m\u00eame addition de palladium ; Grades 16 et 17 sont les options \u00e0 plus faible teneur en palladium.<\/p>\n

Un acide plus concentr\u00e9 est-il toujours plus d\u00e9favorable ?<\/strong> Non, et c'est l'hypoth\u00e8se erron\u00e9e la plus fr\u00e9quente pour ce service. Dans l'acide nitrique bouillant, la courbe TIMET atteint un maximum autour de 40 \u00e0 50 pour cent pour les nuances non alli\u00e9es et contenant du palladium, puis diminue vers 70 pour cent, de sorte qu'un flux de concentration moyenne peut constituer des conditions de service plus s\u00e9v\u00e8res qu'un flux concentr\u00e9.<\/p>\n

Le titane peut-il \u00eatre utilis\u00e9 dans l'acide nitrique rouge fumant ?<\/strong> Non. Les recommandations publi\u00e9es l'excluent en raison du risque de r\u00e9action pyrophorique. Traitez ce cas comme une exclusion de s\u00e9curit\u00e9 des proc\u00e9d\u00e9s.<\/p>\n

Pourquoi mon coupon de laboratoire a-t-il donn\u00e9 un r\u00e9sultat plus d\u00e9favorable que l'installation ?<\/strong> Tr\u00e8s probablement en raison de l'effet du titane dissous. Dans les essais TIMET de 24 heures, le passage de 0 \u00e0 40 mg\/l d'ions titane a fait passer la vitesse dans l'acide \u00e0 68 pour cent de 31.8 mpy \u00e0 0.4 mpy. L'acide neuf dans un essai court ne b\u00e9n\u00e9ficie d'aucune de cette inhibition.<\/p>\n

Qu'en est-il des acides r\u00e9ducteurs tels que l'acide chlorhydrique ou sulfurique ?<\/strong> C'est le cas inverse et il n\u00e9cessite une nuance diff\u00e9rente. Voir Titane Grade 7 dans les acides r\u00e9ducteurs<\/a>.<\/p>\n

Quelle norme s'applique au mat\u00e9riau ?<\/strong> La plaque et la t\u00f4le sont conformes \u00e0 ASTM B265, le tube \u00e0 ASTM B338, la barre \u00e0 ASTM B348. Le guide des plaques est disponible \u00e0 l'adresse le guide ASTM B265 des t\u00f4les et plaques<\/a>.<\/p>\n

Envoyez les donn\u00e9es du fluide avec la demande de prix<\/h2>\n

Envoyez la plage de concentration d'acide, la temp\u00e9rature, si la surface est chauff\u00e9e, la phase liquide ou vapeur, la recirculation, les contaminants, ainsi que la nuance, la norme, les dimensions et la quantit\u00e9 \u00e0 la page de demande de prix de Beiyu<\/a>. R\u00e9vis\u00e9 par Penn Ma<\/a>, 15 ans d'exportation de produits d'usine en titane. Derni\u00e8re r\u00e9vision : 2026-09-02.<\/p>","protected":false},"excerpt":{"rendered":"

In boiling 90 percent nitric acid on a heating surface, the tests published by TIMET put unalloyed titanium at 1.0 to 6.6 mpy (0.03 to 0.17 mm\/y) while Type 304L stainless ran 150 to 2,900 mpy (3.8 to 73.7 mm\/y) in the same TIMET tests. That two-to-three order of magnitude gap is why nitric acid […]<\/p>\n","protected":false},"author":2,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_templately_pack_id":"","_templately_imported_at":"","_templately_source":"","_templately_import_session_id":"","site-sidebar-layout":"default","site-content-layout":"","ast-site-content-layout":"default","site-content-style":"default","site-sidebar-style":"default","ast-global-header-display":"","ast-banner-title-visibility":"","ast-main-header-display":"","ast-hfb-above-header-display":"","ast-hfb-below-header-display":"","ast-hfb-mobile-header-display":"","site-post-title":"","ast-breadcrumbs-content":"","ast-featured-img":"","footer-sml-layout":"","ast-disable-related-posts":"","theme-transparent-header-meta":"","adv-header-id-meta":"","stick-header-meta":"","header-above-stick-meta":"","header-main-stick-meta":"","header-below-stick-meta":"","astra-migrate-meta-layouts":"default","ast-page-background-enabled":"default","ast-page-background-meta":{"desktop":{"background-color":"var(--ast-global-color-5)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"ast-content-background-meta":{"desktop":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"var(--ast-global-color-4)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"footnotes":""},"categories":[27,137],"tags":[],"class_list":["post-6032","post","type-post","status-publish","format-standard","hentry","category-news","category-technical-guides"],"yoast_head":"\nTitanium in Nitric Acid: Rates and Hard Limits | Beiyu<\/title>\n<meta name=\"description\" content=\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\" \/>\n<meta name=\"robots\" content=\"index, follow, max-snippet:-1, max-image-preview:large, max-video-preview:-1\" \/>\n<link rel=\"canonical\" href=\"https:\/\/beiyutitanium.com\/fr\/titanium-in-nitric-acid\/\" \/>\n<meta property=\"og:locale\" content=\"fr_FR\" \/>\n<meta property=\"og:type\" content=\"article\" \/>\n<meta property=\"og:title\" content=\"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu\" \/>\n<meta property=\"og:description\" content=\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\" \/>\n<meta property=\"og:url\" content=\"https:\/\/beiyutitanium.com\/fr\/titanium-in-nitric-acid\/\" \/>\n<meta property=\"og:site_name\" content=\"Beiyu Titanium\" \/>\n<meta property=\"article:published_time\" content=\"2026-09-02T23:10:00+00:00\" \/>\n<meta property=\"article:modified_time\" content=\"2026-09-02T23:55:10+00:00\" \/>\n<meta property=\"og:image\" content=\"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/06\/grade-12-titanium-weld-neck-flange-astm-b381-asme-b16-5-scaled.jpg\" \/>\n\t<meta property=\"og:image:width\" content=\"1200\" \/>\n\t<meta property=\"og:image:height\" content=\"999\" \/>\n\t<meta property=\"og:image:type\" content=\"image\/jpeg\" \/>\n<meta name=\"author\" content=\"Penn Ma\" \/>\n<meta name=\"twitter:card\" content=\"summary_large_image\" \/>\n<meta name=\"twitter:label1\" content=\"Written by\" \/>\n\t<meta name=\"twitter:data1\" content=\"Penn Ma\" \/>\n\t<meta name=\"twitter:label2\" content=\"Est. reading time\" \/>\n\t<meta name=\"twitter:data2\" content=\"11 minutes\" \/>\n<script type=\"application\/ld+json\" class=\"yoast-schema-graph\">{\"@context\":\"https:\\\/\\\/schema.org\",\"@graph\":[{\"@type\":\"Article\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#article\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"},\"author\":{\"name\":\"Penn Ma\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/person\\\/3560db17cf08813edf34f012735b971b\"},\"headline\":\"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits\",\"datePublished\":\"2026-09-02T23:10:00+00:00\",\"dateModified\":\"2026-09-02T23:55:10+00:00\",\"mainEntityOfPage\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"},\"wordCount\":2327,\"publisher\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\"},\"articleSection\":[\"News\",\"Technical Guides\"],\"inLanguage\":\"fr-FR\"},{\"@type\":\"WebPage\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\",\"name\":\"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#website\"},\"datePublished\":\"2026-09-02T23:10:00+00:00\",\"dateModified\":\"2026-09-02T23:55:10+00:00\",\"description\":\"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.\",\"breadcrumb\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#breadcrumb\"},\"inLanguage\":\"fr-FR\",\"potentialAction\":[{\"@type\":\"ReadAction\",\"target\":[\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/\"]}]},{\"@type\":\"BreadcrumbList\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/titanium-in-nitric-acid\\\/#breadcrumb\",\"itemListElement\":[{\"@type\":\"ListItem\",\"position\":1,\"name\":\"Home\",\"item\":\"https:\\\/\\\/beiyutitanium.com\\\/\"},{\"@type\":\"ListItem\",\"position\":2,\"name\":\"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits\"}]},{\"@type\":\"WebSite\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#website\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/\",\"name\":\"Beiyu Titanium\",\"description\":\"Certified titanium materials and custom components for aerospace, medical, chemical, and industrial applications.\",\"publisher\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\"},\"potentialAction\":[{\"@type\":\"SearchAction\",\"target\":{\"@type\":\"EntryPoint\",\"urlTemplate\":\"https:\\\/\\\/beiyutitanium.com\\\/?s={search_term_string}\"},\"query-input\":{\"@type\":\"PropertyValueSpecification\",\"valueRequired\":true,\"valueName\":\"search_term_string\"}}],\"inLanguage\":\"fr-FR\"},{\"@type\":\"Organization\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#organization\",\"name\":\"Beiyu Titanium\",\"alternateName\":\"\u5317\u9a6d\u949b\u4e1a\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/\",\"logo\":{\"@type\":\"ImageObject\",\"inLanguage\":\"fr-FR\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/logo\\\/image\\\/\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/wp-content\\\/uploads\\\/2026\\\/03\\\/logo4.png\",\"contentUrl\":\"https:\\\/\\\/beiyutitanium.com\\\/wp-content\\\/uploads\\\/2026\\\/03\\\/logo4.png\",\"width\":429,\"height\":116,\"caption\":\"Beiyu Titanium\"},\"image\":{\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/logo\\\/image\\\/\"},\"sameAs\":[\"https:\\\/\\\/www.linkedin.com\\\/company\\\/113015050\\\/\",\"https:\\\/\\\/www.youtube.com\\\/channel\\\/UC4Rr5qjUmKbbnROzU8zwluQ\",\"https:\\\/\\\/www.instagram.com\\\/beiyutrade\\\/\",\"https:\\\/\\\/www.facebook.com\\\/people\\\/Beiyu-Titanium-Group\\\/61580787646046\\\/\",\"https:\\\/\\\/www.crunchbase.com\\\/organization\\\/beiyu-titanium\",\"https:\\\/\\\/www.wikidata.org\\\/wiki\\\/Q140386451\"],\"contactPoint\":{\"@type\":\"ContactPoint\",\"contactType\":\"sales\",\"email\":\"penn@beiyutitanium.com\",\"availableLanguage\":[\"English\",\"Chinese\"]},\"description\":\"Beiyu Titanium (legal entity Jiaxing Beiyu New Materials Technology Co., Ltd.) is a China-based supplier and exporter of ASTM and AMS titanium bar, plate, sheet, tube, pipe, forgings, flanges, fasteners and custom machined parts, plus nickel and Inconel alloys, for chemical, marine, medical and industrial buyers worldwide. Production runs through the Beiyu titanium mill in Baoji, Shaanxi. Orders are RFQ-based, with EN 10204 3.1 mill test certificates and heat-number traceability available on request.\",\"areaServed\":\"Worldwide\",\"knowsAbout\":[\"Titanium\",\"Titanium alloy\",\"Titanium bar\",\"Titanium sheet and plate\",\"Titanium tube and pipe\",\"Titanium forgings\",\"Titanium wire\",\"Titanium anode\"],\"address\":{\"@type\":\"PostalAddress\",\"streetAddress\":\"Baotai Road Industrial Park, High-tech Development Zone\",\"addressLocality\":\"Baoji\",\"addressRegion\":\"Shaanxi\",\"addressCountry\":\"CN\"},\"legalName\":\"Jiaxing Beiyu New Materials Technology Co., Ltd.\"},{\"@type\":\"Person\",\"@id\":\"https:\\\/\\\/beiyutitanium.com\\\/#\\\/schema\\\/person\\\/3560db17cf08813edf34f012735b971b\",\"name\":\"Penn Ma\",\"image\":{\"@type\":\"ImageObject\",\"inLanguage\":\"fr-FR\",\"@id\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"url\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"contentUrl\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g\",\"caption\":\"Penn Ma\"},\"description\":\"Penn Ma is the person who answers the RFQs at Beiyu Titanium. Over 15 years in titanium export he has learned to review each specification line himself, checking grade, standard, dimensions, tolerance and certificate scope against mill capability before quoting, rather than routing enquiries through a sales desk. He came to titanium supply from the other side of the transaction. Before leading Beiyu's international business he worked at Koch (Koch-Glitsch) and was directly involved in delivering a SABIC petrochemical project in Fujian, China. That work was built on inspection and test plans, material certification and heat traceability, third party inspection coordination, and project documentation and dossier control. Those are the same four things a process industry or regulated buyer will hold a titanium supplier to, and having had to enforce them as a customer is why they are treated here as part of the supply rather than as paperwork produced afterwards. His day-to-day work spans the questions this site is written to answer: choosing between commercially pure and alloyed titanium grades for a corrosive service, reading a mill test certificate against the ordered standard, and matching a buyer's designation (ASTM grade, UNS, German Werkstoff number or French NF code) to the same metal across markets. Beiyu supplies titanium, nickel-alloy and refractory mill products across bar, rod, plate, tube, block, ring, coil, ingot, forgings and machined parts, with EN 10204 3.1 documentation and heat-number traceability.\",\"url\":\"https:\\\/\\\/beiyutitanium.com\\\/fr\\\/author\\\/penn-ma\\\/\"}]}<\/script>\n<!-- \/ Yoast SEO plugin. -->","yoast_head_json":{"title":"Titane dans l'acide nitrique : vitesses et limites strictes | Beiyu","description":"Vitesses de corrosion publi\u00e9es pour le titane dans l'acide nitrique : le pic \u00e0 concentration interm\u00e9diaire, pourquoi les ions m\u00e9talliques dissous inhibent, la phase vapeur et la fen\u00eatre de composition rouge fumante.","robots":{"index":"index","follow":"follow","max-snippet":"max-snippet:-1","max-image-preview":"max-image-preview:large","max-video-preview":"max-video-preview:-1"},"canonical":"https:\/\/beiyutitanium.com\/fr\/titanium-in-nitric-acid\/","og_locale":"fr_FR","og_type":"article","og_title":"Titanium in Nitric Acid: Rates and Hard Limits | Beiyu","og_description":"Published corrosion rates for titanium in nitric acid: the mid-concentration peak, why dissolved metal ions inhibit, vapour phase, and the red fuming composition window.","og_url":"https:\/\/beiyutitanium.com\/fr\/titanium-in-nitric-acid\/","og_site_name":"Beiyu Titanium","article_published_time":"2026-09-02T23:10:00+00:00","article_modified_time":"2026-09-02T23:55:10+00:00","og_image":[{"width":1200,"height":999,"url":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/06\/grade-12-titanium-weld-neck-flange-astm-b381-asme-b16-5-scaled.jpg","type":"image\/jpeg"}],"author":"Penn Ma","twitter_card":"summary_large_image","twitter_misc":{"Written by":"Penn Ma","Est. reading time":"11 minutes"},"schema":{"@context":"https:\/\/schema.org","@graph":[{"@type":"Article","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#article","isPartOf":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"},"author":{"name":"Penn Ma","@id":"https:\/\/beiyutitanium.com\/#\/schema\/person\/3560db17cf08813edf34f012735b971b"},"headline":"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits","datePublished":"2026-09-02T23:10:00+00:00","dateModified":"2026-09-02T23:55:10+00:00","mainEntityOfPage":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"},"wordCount":2327,"publisher":{"@id":"https:\/\/beiyutitanium.com\/#organization"},"articleSection":["News","Technical Guides"],"inLanguage":"fr-FR"},{"@type":"WebPage","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/","url":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/","name":"Titane dans l'acide nitrique : vitesses et limites strictes | Beiyu","isPartOf":{"@id":"https:\/\/beiyutitanium.com\/#website"},"datePublished":"2026-09-02T23:10:00+00:00","dateModified":"2026-09-02T23:55:10+00:00","description":"Vitesses de corrosion publi\u00e9es pour le titane dans l'acide nitrique : le pic \u00e0 concentration interm\u00e9diaire, pourquoi les ions m\u00e9talliques dissous inhibent, la phase vapeur et la fen\u00eatre de composition rouge fumante.","breadcrumb":{"@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#breadcrumb"},"inLanguage":"fr-FR","potentialAction":[{"@type":"ReadAction","target":["https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/"]}]},{"@type":"BreadcrumbList","@id":"https:\/\/beiyutitanium.com\/titanium-in-nitric-acid\/#breadcrumb","itemListElement":[{"@type":"ListItem","position":1,"name":"Home","item":"https:\/\/beiyutitanium.com\/"},{"@type":"ListItem","position":2,"name":"Titanium in Nitric Acid: Rates, the Mid-Range Peak, and the Hard Limits"}]},{"@type":"WebSite","@id":"https:\/\/beiyutitanium.com\/#website","url":"https:\/\/beiyutitanium.com\/","name":"Beiyu Titanium","description":"Mat\u00e9riaux en titane certifi\u00e9s et composants sur mesure pour les applications a\u00e9ronautiques, m\u00e9dicales, chimiques et industrielles.","publisher":{"@id":"https:\/\/beiyutitanium.com\/#organization"},"potentialAction":[{"@type":"SearchAction","target":{"@type":"EntryPoint","urlTemplate":"https:\/\/beiyutitanium.com\/?s={search_term_string}"},"query-input":{"@type":"PropertyValueSpecification","valueRequired":true,"valueName":"search_term_string"}}],"inLanguage":"fr-FR"},{"@type":"Organization","@id":"https:\/\/beiyutitanium.com\/#organization","name":"Beiyu Titanium","alternateName":"\u5317\u9a6d\u949b\u4e1a","url":"https:\/\/beiyutitanium.com\/","logo":{"@type":"ImageObject","inLanguage":"fr-FR","@id":"https:\/\/beiyutitanium.com\/#\/schema\/logo\/image\/","url":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/03\/logo4.png","contentUrl":"https:\/\/beiyutitanium.com\/wp-content\/uploads\/2026\/03\/logo4.png","width":429,"height":116,"caption":"Beiyu Titanium"},"image":{"@id":"https:\/\/beiyutitanium.com\/#\/schema\/logo\/image\/"},"sameAs":["https:\/\/www.linkedin.com\/company\/113015050\/","https:\/\/www.youtube.com\/channel\/UC4Rr5qjUmKbbnROzU8zwluQ","https:\/\/www.instagram.com\/beiyutrade\/","https:\/\/www.facebook.com\/people\/Beiyu-Titanium-Group\/61580787646046\/","https:\/\/www.crunchbase.com\/organization\/beiyu-titanium","https:\/\/www.wikidata.org\/wiki\/Q140386451"],"contactPoint":{"@type":"ContactPoint","contactType":"sales","email":"penn@beiyutitanium.com","availableLanguage":["English","Chinese"]},"description":"Beiyu Titanium (entit\u00e9 juridique Jiaxing Beiyu New Materials Technology Co., Ltd.) est un fournisseur et exportateur chinois de barres, plaques, t\u00f4les, tubes, pi\u00e8ces forg\u00e9es, brides, \u00e9l\u00e9ments de fixation et pi\u00e8ces usin\u00e9es sur mesure en titane ASTM et AMS, ainsi que d'alliages de nickel et Inconel, destin\u00e9s aux acheteurs des secteurs chimique, maritime, m\u00e9dical et industriel dans le monde entier. La production est assur\u00e9e par l'usine de titane Beiyu \u00e0 Baoji, Shaanxi. Les commandes sont trait\u00e9es sur demande de prix, avec des certificats de r\u00e9ception 3.1 selon EN 10204 et une tra\u00e7abilit\u00e9 par num\u00e9ro de coul\u00e9e disponibles sur demande.","areaServed":"Worldwide","knowsAbout":["Titanium","Titanium alloy","Titanium bar","Titanium sheet and plate","Titanium tube and pipe","Titanium forgings","Titanium wire","Titanium anode"],"address":{"@type":"PostalAddress","streetAddress":"Baotai Road Industrial Park, High-tech Development Zone","addressLocality":"Baoji","addressRegion":"Shaanxi","addressCountry":"CN"},"legalName":"Jiaxing Beiyu New Materials Technology Co., Ltd."},{"@type":"Person","@id":"https:\/\/beiyutitanium.com\/#\/schema\/person\/3560db17cf08813edf34f012735b971b","name":"Penn Ma","image":{"@type":"ImageObject","inLanguage":"fr-FR","@id":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","url":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","contentUrl":"https:\/\/secure.gravatar.com\/avatar\/0659bdefb633d0d8e567b06d2f8bffac2a369834e53e96c922a06fd8a96f3c72?s=96&d=mm&r=g","caption":"Penn Ma"},"description":"Penn Ma est la personne qui r\u00e9pond aux demandes de prix chez Beiyu Titanium. Avec plus de 15 ans d'exp\u00e9rience dans l'exportation de titane, il a appris \u00e0 examiner lui-m\u00eame chaque ligne de sp\u00e9cification, en v\u00e9rifiant la nuance, la norme, les dimensions, la tol\u00e9rance et le p\u00e9rim\u00e8tre du certificat par rapport aux capacit\u00e9s de l'usine avant d'\u00e9tablir une offre, plut\u00f4t que d'orienter les demandes vers un service commercial. Il est venu \u00e0 l'approvisionnement en titane depuis l'autre c\u00f4t\u00e9 de la transaction. Avant de diriger les activit\u00e9s internationales de Beiyu, il a travaill\u00e9 chez Koch (Koch-Glitsch) et a particip\u00e9 directement \u00e0 la r\u00e9alisation d'un projet p\u00e9trochimique SABIC dans le Fujian, en Chine. Ce travail reposait sur des plans de contr\u00f4le et d'essais, la certification des mat\u00e9riaux et la tra\u00e7abilit\u00e9 par num\u00e9ro de coul\u00e9e, la coordination du contr\u00f4le par tierce partie, ainsi que le contr\u00f4le de la documentation et des dossiers de projet. Ce sont les quatre m\u00eames \u00e9l\u00e9ments qu'un acheteur de l'industrie des proc\u00e9d\u00e9s ou un acheteur soumis \u00e0 r\u00e9glementation exigera d'un fournisseur de titane, et le fait d'avoir d\u00fb les faire appliquer en tant que client explique qu'ils soient trait\u00e9s ici comme faisant partie de la fourniture plut\u00f4t que comme des documents produits ult\u00e9rieurement. Son travail quotidien couvre les questions auxquelles ce site est destin\u00e9 \u00e0 r\u00e9pondre : choisir entre des nuances de titane commercialement pur et alli\u00e9 pour un service corrosif, lire un certificat mati\u00e8re par rapport \u00e0 la norme command\u00e9e, et faire correspondre la d\u00e9signation d'un acheteur (nuance ASTM, UNS, num\u00e9ro Werkstoff allemand ou code NF fran\u00e7ais) au m\u00eame m\u00e9tal sur diff\u00e9rents march\u00e9s. Beiyu fournit des produits d'usine en titane, alliages de nickel et m\u00e9taux r\u00e9fractaires, notamment des barres, tiges, plaques, tubes, blocs, anneaux, bobines, lingots, pi\u00e8ces forg\u00e9es et pi\u00e8ces usin\u00e9es, avec documentation EN 10204 3.1 et tra\u00e7abilit\u00e9 par num\u00e9ro de coul\u00e9e.","url":"https:\/\/beiyutitanium.com\/fr\/author\/penn-ma\/"}]}},"_links":{"self":[{"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/posts\/6032","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/comments?post=6032"}],"version-history":[{"count":1,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/posts\/6032\/revisions"}],"predecessor-version":[{"id":6033,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/posts\/6032\/revisions\/6033"}],"wp:attachment":[{"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/media?parent=6032"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/categories?post=6032"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/beiyutitanium.com\/fr\/wp-json\/wp\/v2\/tags?post=6032"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}